    Default Aluminum Welding questions?

    Hey guys, i looked in the search feature but can't get answers to the following questions. I have a MM 210 and have just bought a 3035 spoolgun to do aluminum. Most of the welding i do will be 1/8" square tubing to build a couple trailers and a headache rack for my truck. It will mostly be 2x2 or 1.5 x 1.5 tubing for the trailers racks. Now for the questions..
    1) Does the metal need to be preheated? If so how - with a propane torch or something?
    2) Do i use 4043 or 5356 aluminum. Whats the real differences with the two. Can i mix and match the two. If i have a spool of 5356, can it be used on a piece of 4043?
    3) What does push/pull mean. I read alot about it but cant find out what it means. Is the push/pull gun the spoolgun?
    4) And finally when welding aluminum, do i go from left to right, or right to left? Do i keep the arc in the puddle or away from it, thanks.

  2. #2
    Join Date
    Sep 2005
    Location
    Salem ,Ohio
    Posts
    3,898

    Default

    1/8" really dosen't need a preheat but a propane torch works great.

    4043 is usually what is found on a suppliers shelf.

    Push pull is the gun because it has a motor to pull the wire thru. Instead of pushing from the welders drive and up the mig cable.

    I go from right to left because i can see the puddle better. Keep the gun at a slight angle just back off of 90 degrees like 80 or so and push the wire into the puddle.

    I don't weld that much 5356 and if i do i don't know it and use 4043 on it because thats all i use....Bob
    Bob Wright, Grandson of Tee Nee Boat Trailer Founder
    Metal Master Fab Salem, Oh 44460
    Birthplace of the Silver & Deming Drill
    1999 MM185 w/185 Spoolgun,1986 Thunderbolt AC/DC
    Spool Gun conversion. How To Do It. Below.
    http://www.millerwelds.com/resources...php?albumid=48

  3. #3
    Join Date
    Aug 2007
    Location
    arkansas
    Posts
    781

    Default

    alright, with a push pull set up, the feeder and the gun has a separate set of drives. the gun drive is actually the control and the drive in the feeder is the slave. the xr-a and the xr-edge is an example of push-pull...

    on 1/8 material, preheat is absolutely not necessary. i dont even preheat on 3/4 inch but the mm210 is not heavy enough for that... you will probably run about 190 amps for 1/8 and be sure to have your running shoes on...you'll need to move quickly...

    the biggest difference that i have found between 4043 and 5356 is that the 4043 is a little more fluid of a puddle, the 5356 is easier to feed with less "bird hotels" if you are going to post heat treat your welds, then you must use 4043 alloy. if you are going to anodize then you must use 5356. on a non post heat treated weld, the 5356 is actually a stronger weld...i have never tried to mix the alloys and i am not sure that i would recommend it at all. if your parent metal is 6061, either will do nicely.

    when welding aluminum, it does not matter the direction of travel except vertical down. lead into the weld with about 3/8 stick-out and a push angle of about 5 to 7 degrees. do not use any torch manipulation, only a straight stringer bead. when done properly, your weld will have a v-shaped bead raised slightly in the center and be fairly shiny.

    as always, turn it up and burn it in... if you think that you might be hot enough, turn it up a little more and move faster...lol


    hope that i could help a little, if you have any more questions, just ask...
    welder_one

    nothing fancy, just a few hot glue guns for metal
    www.sicfabrications.com

  4. #4
    Join Date
    Nov 2007
    Location
    Saskatoon, Sask, Canada
    Posts
    1,270

    Default

    Great advice from both guys. 4043 will be easier to make a nice looking weld with. Practice, practice, practice and have fun with it... oh yeah I'll remind you one more time, push on aluminum don't drag/pull.
    at home:
    2012 325 Trailblazer EFI with Excel power
    2007 302 Trailblazer with the Robin FOR SALE
    2008 Suitcase 12RC
    Spoolmatic 30A
    WC-24
    2009 Dynasty 200DX
    2000 XMT 304
    2008 Thermal Dynamics Cutmaster 52
    Sold:MM130XP
    Sold:MM 251
    Sold:CST 280

    at work:
    Invision 350MP
    Dynasty 350
    Millermatic 350P
    Retired:Shopmaster 300 with a HF-251

  5. #5
    Join Date
    May 2007
    Posts
    20

    Default

    so i did my first welds on aluminum on a bunch of new scrap pieces i got from the local metal depot. I had the welder set at 4 and 70, miller 210, and the argon gas at 35 cf. It looks not bad, except around the welds the aluminum is like covered in a layer of brown and black soot. I can't find on this forum what is causing this. I can take a picture if i need to. Help!

  6. #6
    Join Date
    Aug 2007
    Location
    Seattle,WA
    Posts
    55

    Default

    You can take your gas pressure down to around 15 or 20 cfh. You will always have some black soot around your welds most of the time. There will be even more if you switch to 5356. It's just part of the process.
    Welders do it hotter!!
    www.Munsonworks.com

  7. #7
    Join Date
    Mar 2007
    Location
    Vero Beach, fl.
    Posts
    761

    Default droptopgt

    With the questions you are asking you are nowhere ready to start building trailers and sending them out on our highways. I'm surprised no one else has mentioned this yet. It seems pretty clear to me that you have not done any work with aluminum and putting something out on the street with millions of other people is just looking for trouble in my opinion.

    Get your self some practice with something other than structural or vehicular type projects. I'm not trying to be rude or put you down, just thinking of the safety of the general public. Too many things are cruising down the highways that are poorly constructed, poorly welded, or just plain out unsafe. Just wait a while and gain some experience before you take on the task of building something that could possibly put yourself or others in harms way. Dave
    Last edited by dabar39; 01-24-2008 at 08:36 AM. Reason: spelling
    If necessity is the Mother of Invention, I must be the Father of Desperation!

    John Blewett III 10-22-73 to 8-16-07
    Another racing great gone but not to be forgotten.http://video.google.com/videoplay?do...modified&hl=en

  8. #8
    Join Date
    Aug 2007
    Location
    Seattle,WA
    Posts
    55

    Default

    I would have to agree with DaBar. I have been welding aluminum for about 2 1/2 years and I am still very cautious when doing it. I have faith in my self that I am doing everything the right way and taking the necessary steps to check myself but I would still be a little apprehensive to weld anything that would be getting pulled down a freeway.
    Welders do it hotter!!
    www.Munsonworks.com

  9. #9
    Join Date
    Sep 2005
    Location
    Salem ,Ohio
    Posts
    3,898

    Cool

    You have smut. Here are a few tips to get rid of it....Bob
    http://www.thefabricator.com/Aluminu...cle.cfm?ID=554
    Bob Wright, Grandson of Tee Nee Boat Trailer Founder
    Metal Master Fab Salem, Oh 44460
    Birthplace of the Silver & Deming Drill
    1999 MM185 w/185 Spoolgun,1986 Thunderbolt AC/DC
    Spool Gun conversion. How To Do It. Below.
    http://www.millerwelds.com/resources...php?albumid=48

  10. #10
    Join Date
    Nov 2006
    Location
    Lake of the Ozarks MO
    Posts
    3,534

    Default

    I also agree that trailers and such is NOT the place to learn to weld aluminum.
    I weld aluminum in my own biz for several years now and I can assure you that aluminum is a poor material to make trailers with unless it is an engineered design. Even then it still has a limited life span.
    If you look at GOOD aluminum boat trailers you will see they are bolted and never welded. Welding removes the temper and it is very expensive to get it back.
    Miller Dynasty 700...OH YEA BABY!!
    MM 350P...PULSE SPRAYIN' MONSTER
    Miller Dynasty 200 DX "Blue Lightning"

    Miller Bobcat 225 NT
    Miller 30-A Spoolgun
    Miller WC-115-A
    Miller Spectrum 300
    Miller Spoolmate 200
    Miller 225 Thunderbolt
    SPEEDGLAS 9100XX

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •  

Warning: Non-static method PhpQuickProfiler::getMicroTime() should not be called statically in /mnt/stor3-wc1-dfw1/357822/357839/www.millerwelds.com/web/content/lib/pqp/classes/Console.php on line 77

Warning: Non-static method PhpQuickProfiler::getMicroTime() should not be called statically in /mnt/stor3-wc1-dfw1/357822/357839/www.millerwelds.com/web/content/lib/pqp/classes/Console.php on line 77

Warning: Non-static method PhpQuickProfiler::getMicroTime() should not be called statically in /mnt/stor3-wc1-dfw1/357822/357839/www.millerwelds.com/web/content/lib/pqp/classes/Console.php on line 77

Warning: Non-static method PhpQuickProfiler::getMicroTime() should not be called statically in /mnt/stor3-wc1-dfw1/357822/357839/www.millerwelds.com/web/content/lib/pqp/classes/Console.php on line 77

Warning: Non-static method PhpQuickProfiler::getMicroTime() should not be called statically in /mnt/stor3-wc1-dfw1/357822/357839/www.millerwelds.com/web/content/lib/pqp/classes/Console.php on line 77

Warning: Non-static method PhpQuickProfiler::getMicroTime() should not be called statically in /mnt/stor3-wc1-dfw1/357822/357839/www.millerwelds.com/web/content/lib/pqp/classes/Console.php on line 77

Warning: Non-static method PhpQuickProfiler::getMicroTime() should not be called statically in /mnt/stor3-wc1-dfw1/357822/357839/www.millerwelds.com/web/content/lib/pqp/classes/Console.php on line 77

Warning: Function split() is deprecated in /mnt/stor3-wc1-dfw1/357822/357839/www.millerwelds.com/web/content/lib/footer.inc.php on line 82

Welding Projects

Special Offers: See the latest Miller deals and promotions.