Wondering, if a copper backing plate would help dissipate some of the heat to slow the melt down a bit?
Results 11 to 20 of 20
Thread: Aluminum tig joint problem.
09-10-2008, 08:09 PM #11Senior Member
- Join Date
- Jan 2007
- Montana, USA
09-10-2008, 10:21 PM #12Ed Conley
Passport Plus w/Spool Gun
Miller 125c Plasma 120v
SO 2020 Bender
You can call me Bacchus
09-11-2008, 07:12 AM #13
6" x .125 round disk set inside a 6" ID tube set flush with the end and a very tight seam. When I heated the joint and as it started to puddle, the edges of each piece melted back away from the seam line leaving a void. If I applied a little filler to bring the two molten edges together, then I could continue without filler if I was careful but the weld was flat and no real strength. So......how does one make a tack weld when this happens?
Miller 252 Mig
Miller Cricket XL
Millermatic 150 Mig
Miller Syncrowave 200 Tig
Jet Lathe and Mill
Jet 7x12 horz/vert band saw
DeWalt Multi Cutter metal saw
Century 50 Amp Plasma Cutter
20 ton electric/hydraulic vertical press
60" X 60" router/plasma table
Vist my site: www.nixstuff.com
and check out some of my ironwork and other stuff
09-11-2008, 07:33 PM #14Senior Member
- Join Date
- Dec 2007
09-16-2008, 03:49 AM #15
09-16-2008, 05:09 AM #16
Yeah, hit it with the heat big time. Super clean material, tight fit, electrode angle are all key.
For the flush fit you mention I would probably have the electrode roughly parallel with the disc, pushing the pipe material towards the disc with the arc."If you build it, they will come!"
05-17-2009, 07:31 PM #17
But rather than burning yourself up with this, when we all know you obviously have good knowledge to contribute, why not let it go?
You are just skirting the edge of forum rules if not disobeying them and it generally ruins the entire mood here and really does not make you any real friends either.
It is one thing to make a snide comment here or there but to dig up old threads and call someone out is actually nothing more than harrassment plain and simple. No matter who started it, and I doubt anyone cares it is beginning to get out of hand now.
If Monte wants to watch Hawks or raise flowers and post about it then it just shows maybe we could have an off topic section.
I spend enuff time on here I have grown to respect the opinions of many members on a broad variety of subjects besides just welding. Monte is simply sharing his. There are a ton of threads I simply do not read because I have no interest in them.
So as nothing other than just one forum member to another....could you just let this go PLEASE and help keep the peace here at miller?? We have already had enuff drama here for several forums
Miller Dynasty 700...OH YEA BABY!!
MM 350P...PULSE SPRAYIN' MONSTER
Miller Dynasty 200 DX "Blue Lightning"
Miller Bobcat 225 NT (what I began my present Biz with!)
Miller 30-A Spoolgun
Miller Spectrum 300
Miller 225 Thunderbolt (my first machine bought new 1980)
05-17-2009, 07:44 PM #18Senior Member
- Join Date
- Dec 2007
I did these aluminum cubes in almost the same way as your round tube setup.
The material is 1/8" thick and the finished cubes are 3 1/4" on each side.
Since the material is 3" wide, I cut the pieces 3" long.
Tacked the 4 sides together leaving a 3" x 3" opening for each "plug"
Then I had to figure out how to keep the plug from falling in.
Used a small 2" diameter rod and a stack of washers inside to get the aluminum plug to end up 1/8" higher than the sides.
Then used filler rod to do an outside corner weld which was easier for me to do.
So it is not exactly like your situation.
If I had to do your weld, I would have the round plug stick up above the edge of the pipe and do the same outside weld with filler rod.
Oh, had to drill the vent hole after I messed up the first one as it was not vented.
Good luckThermal Arc GTSW400, Airco Heliwelder II, Miller Dynasty 350, Hypertherm 1000, oxy-fuel setup, metal cutting bandsaw, air compressor, drill press, etc.:
Call me the "Clouseau" of welding !
05-17-2009, 09:23 PM #19Dynasty 350DX
Dynasty 200DX TigRunner
MM Passport Plus
Spectrum 375 Extreme
08' Trailblazer 302
05-17-2009, 11:02 PM #20Senior Member
- Join Date
- Mar 2007
- Deltaville, VA
Call it a tack, or call it a weld but trying to join two pieces of aluminum without filler will always result in a weld that is weaker than one in which filler was added. Not only do they often crack, the weld itself is just not as strong.
What's the problem with adding a little filler. Dang stuff is really pretty cheap.
Stainless steel, on the other hand, will fuse nicely without filler if the joint is prepared properly.