Thread: How would you fix this leak?
05-15-2007, 12:16 AM #11I'm not late...
I'm just on Hawaiian Time
05-15-2007, 12:19 AM #12Senior Member
- Join Date
- Oct 2006
- DFW area
I don't know if they're still around, but years ago when I did alot of commercial plumbing, the Plumbing Supply and/or Air Conditioner Supply houses had a clamp-on patch for doing that on a 'live' water system.
We'd get a leak in a chill water AC system, and use them as a permanant repair 'till Winter came along and we could shut down & drain the water out for welding the leak like 'normal'.
These patches were a strap of Stainless Steel about a foot long, size specific for the pipe, with a pretty thick neopreme sheet on the inside. The lengthwise edges were rolled up over a bar (on each side)and had nuts & bolts going through every couple of inches. The neopreme was thick enough to use/seal over a leaking weld seam joing two pieces of pipe together also.
We had to use one under a parking lot one time. We dug up/exposed the pipe, patched it, then a few months later, the parking lot got re-surfaced. We couldn't find it again. Rather than dig up a bunch of new parking lot, we just left it. Far as I know, its still holding, and that was about 10 years ago.
They worked great. All it took to use one was:
Find the leak, clean the area, wrap the patch around the pipe, put the nuts & bolts through, and tighten them down.
."Gone are the days of wooden ships, and Iron men.
I doubt we'll see either of their likes again".
Unknown US Coast Guard unit Commander.
05-15-2007, 02:41 AM #13
Thats how they repair water mains usualy, same exact device. It's also a permanent solution, so you don't have to replace it later if it's instaled properly.
05-15-2007, 07:41 AM #14
Here's a dumb question I see alot of guys use 6010 rods. Why? I have never used 6010. I have used 6011, 6013 alot and 7018 most, but it seems 6010 is mentioned alot. Is there something about it thats good for something special? I know 60xx is 60,000 lbs, and the xx1x is all postion, the xxx0 I think is DC only. So what makes this rod better than say a 6011??Scott
HMW [Heavy Metal welding]
05-15-2007, 07:54 AM #15
I think it might be a territorial issue on rod usage. Down here in Florida ( or at least in my area) the rod of choice is 6011 or 7018 for most applications. I have traveled quite a bit thruogh out the country and each demographic area seems to have their own preferance. Is one really any better than the other? I can't really say as I have had good results with all types of rod, but I personally prefer 6011 as an all purpose rod over the others for general duty type welds. DaveIf necessity is the Mother of Invention, I must be the Father of Desperation!
John Blewett III 10-22-73 to 8-16-07
Another racing great gone but not to be forgotten.http://video.google.com/videoplay?do...modified&hl=en
05-15-2007, 08:59 AM #16
Thats kinda my preference, just didn't know if the 6010 was better in some way, ThanksScott
HMW [Heavy Metal welding]
05-15-2007, 07:08 PM #17
We use 6010 rods up here a lot for root passes on pipe. It is a good choice because we can push the weld through the gap between the lands of the 'v' groove, the rod freezes quickly, and provides weld re-inforcement to the inside of the pipe. The hot pass - usually a 7018 or similiar is used to burn out any slag inclusions, and fill any undercut left behind by the 6010. I use it sometimes for a root pass when doing repairs to accomodate poor fit up when you can't get in there for proper weld prep. My hot pass, extra fill passes, and cap pass are ususally 7018,8018,10018,11018 etc.
I also use 6010 for welding on gauge metal lightboxes etc. when I'm outside to prevent burnthrough or distortion.
I am not a pipeline welder so if I offended anyone, I apologize in advance.
05-16-2007, 12:00 AM #18
6010 is very similar to 6011. It's DC only and is a little less agressive. 6011 is better suited to dirty, painted, and rusty metals. 6011 is AC or DC and has a far less stable arc on AC. 6010 is smoother running and for most ppl. has more control over the arc. I always choose 6010 over 6011 unless it's crummy metal then I'll use 6011. Also you can take either one (6011 preferably) and quick dip the rod in water then crank your machine all the way and use it for severing plates and stuff. The water gives it a more agressive arc and alows for better cutting. It actualy works realy well for non critical stuff and quick fixes when decent cutting tools arn't availale.
05-30-2007, 07:31 PM #19
I hope this helps.Triggerman
Ammonia refrigeration tech
Trailblazer 302 (yes, it's new)
Millermatic 180 w/Autoset
HF-15 High frequency
XR15 w/Push-Pull Gun
Victor O/A, DeWalt, North mask
"A professional knows what to do. A craftsman knows why."
05-31-2007, 06:02 AM #20
Next time you run acroos this problem try sharping a drift punch, drive it into the hole until the water stops, weld around it and cut it off. We have done this many times on process water, chill water and even high pressure gas.