  • stainless & mild steel welding

    14ga SS Welded to 14ga. MS . Panels would it be safe to weld. With just. C25. And mild steel mig wire. To keep cost of consumable down.
    .
    Miller Bobcat 225NT onan
    Millermatic 211
    Spoolmate 100
    (Retapped to fit regular mig tips)
    Work better & less parts to stock.
    Miller 130xp
    T/A Dragster 85 (portability 11 pounds)
    Oxygen/Acetylene torch set 50'
    2. 4-1/2" grinders
    1. 9" grinder
    14" Makita chop saw
    1/2" Aircat impact gun 900#

  • #2
    It depends on your definition of "safe". Will you be able to run an actual bead and cause fusion of the base metals? Yup, think so. But there are likely better procedures for it than just using mild steel wire on C25.
    HTP Invertig221 D.V. Water-cooled
    Eastwood MIG175 w/spoolgun
    Eastwood Versacut40 Plasma cutter

    Comment


    • #3
      309 is a better choice for joining stainless and mild steel.

      Comment


      • #4
        It will work but the weld will rust...Bob
        Bob Wright

        Spool Gun conversion. How To Do It. Below.
        http://www.millerwelds.com/resources...php?albumid=48

        Comment


        • #5
          Originally posted by eecervantes83 View Post
          14ga SS Welded to 14ga. MS . Panels would it be safe to weld. With just. C25. And mild steel mig wire. To keep cost of consumable down.
          Maybe. Is someone's life depending on the weld?
          What is the alloy of the stainless? What does it do?
          How thick are the panels? What is their purpose?
          I seldom let my customers decide what procedures to use just to save money, because when it goes wrong it's always on me. I like being the high dollar guy that people would rather not call unless they don't know what to do. It makes me lots more money. Win-Win
          If safe means will it fuse and hold, then your chances are pretty good. The mild steel filler will dilute into the stainless base metal and good chance weaken it.
          309 is generally used to join stainless to carbon steel
          Stainless exhaust pipe gets welded everyday with mild steel wire on cars.
          It may last forever.

          www.facebook.com/outbackaluminumwelding
          Miller Dynasty 700...OH YEA BABY!!
          MM 350P...PULSE SPRAYIN' MONSTER
          Miller Dynasty 280 with AC independent expansion card
          Miller Dynasty 200 DX "Blue Lightning"

          Miller Bobcat 225 NT (what I began my present Biz with!)
          Miller 30-A Spoolgun
          Miller WC-115-A
          Miller Spectrum 300
          Miller 225 Thunderbolt (my first machine bought new 1980)
          Miller Digital Elite Titanium 9400

          Comment


          • #6
            I wouldn't use mild steel if it's not been cold formed. Even then corrosion resistance is pretty poor. Maybe you could harden them otherwise? Or just use a stainless steel grade as Fusionking has already suggested, 309. I'd definitely invest in a better material either way.
            Last edited by koolaid; 11-29-2017, 03:12 AM.

            Comment


            • #7
              Unless this is something not critical, in which case you just need it to stick together soundly without worrying about maximum strength or corrosion resistance. Can't really recommend more expensive material not already in possession without knowing what the project is.