I'm gonna attempt to post some pics of my welding at work. I had to hand weld for a few days as my orbital welder has been tore up . It's good to hand weld once in awhile so I don't lose my hand. This is 347 stainless with the root's welded at 78 amps then I turn my heat up to 86 to fill and cap.I walk my root and second pass then free hand the rest. I'm sure your wondering why freehand , well you can carry ALOT more metal free handing than walking the cup on small o.d. tubing like this. I refer to this type of welding I do as the good ole "hot flop". I just throw it on there and we don't try to make every weld a masterpiece , just not enough time for the pretty stuff. Save the pretty for the weld booth. These welds pass x-ray and thats the bottom line.